molybdenum wire Home - Product - Molybdenum products - molybdenum wire - main

molybdenum wire

1)For wire cutting machine

2)For producing electric light source parts and electric vaccum components

3)For producing heating elements and refractory parts in high temperature furnaces

4)For spraying wear and tear parts of automobile and other machine to enhance their wearability

Tel: +86-15896504204
Description

Purity: 99.95%

Density:>10.2g/cm3

Surface: Molybdenum wire is regular black covered with graphite.After graphite removed,it is metallic luster.

Molybdenum wire size:


Diameter (μm)


Weight (mg/200mm)

Weight (mg/200mg) Tolerance (%)

Diameter Tolerance (%)

Grade 1

Grade 2

Grade 1

Grade 2

20d<30

0.65~1.47

±2.5

±3

30d<40

>1.47~2.61

±2.0

±3

40d<100

>2.61~16.33

±1.5

±3

100d<400

>16.33~256.2

±1.5

±4

400d<600

±1.5

±2.5

600d<3200

±1.0

±2.0

Wire Physical&Mechanical properties

Physical Property

Properties

Metric

Imperial

Density

10.2 g/c

0.369 lb/in³

Melting point

2625

4760°F

Mechanical Properties

Properties

Metric

Imperial

Tensile strength (annealed)

324 MPa

47000 psi

Shear strength (torsional strain rate 0.25/s)

500 MPa

72500 psi

Compressive yield strength (0.01% yield)

400 MPa

58000 psi

Modulus of elasticity

330 GPa

47900 ksi

Modulus of elasticity at elevated temperature (@2000/3630°F)

160 GPa

23200 ksi

Thermal Coefficient of Expansion:

5 x 10-6 cm/cm @ 25O c

Electrical Conductivity:

34% I.A.C.S.

Thermal Conductivity:

1.38 W/cm/K @ 298.2 K

Electrical Resistivity:

5.2 microhm-cm @ 0 oc

Application

1)For wire cutting machine

2)For producing electric light source parts and electric vaccum components

3)For producing heating elements and refractory parts in high temperature furnaces

4)For spraying wear and tear parts of automobile and other machine to enhance their wearability